Effect of natural aging on relaxation behavior and mechanical property of a La-based bulk metallic glass

• Published in: Intermetallics 2021-12, Vol.139, p.107365, Article 107365
• Main Authors: Cui, Xiao, Qiao, Ji Chao, Ma, Yu Bai, Li, Jin Jing, Meng, Xiao Jun, Zu, Fang qiu
• Format: Article
• Language: English
• Subjects: Aging; Aging (natural); Amorphous materials; Bulk metallic glass; Cheese; Compression tests; Crystallization; Dynamic mechanical analysis; Master alloys; Mechanical property; Metallic glasses; Natural aging; Relaxation behavior
• ISSN: 0966-9795; 1879-0216
• DOI: 10.1016/j.intermet.2021.107365

Natural aging, which is the spontaneous temporal evolution of meta-stable systems, is a great task in amorphous materials. In this work, La62Al14(Cu5/6Ag1/6)14(Ni1/2Co1/2)10 BMGs with the same master alloy was prepared 8 years ago and at present. The effect of natural aging on the relaxation behavior and mechanical property of the La-based BMG was studied. Experimental results based on dynamic mechanical analysis and differential scanning calorimetry showed that natural aging for 8 years caused the atomic configuration to relax from a meta-stable state to a relatively more stable state, and the crystallization characteristic was also affected by natural aging. The results of compression testing indicated that the plasticity of the La-based BMG would be reduced, as a result of structural relaxation caused by natural aging. •Eight years natural aging effect of a La-based bulk metallic glass was studied.•Natural aging caused the atomic configuration to relax from a meta-stable state to a relatively more stable state.•The plasticity of the La-based BMG was reduced as the result of natural aging.