Al–Mn–Fe intermetallic formation in AZ91 magnesium alloys: Effects of impurity iron

The influence of iron on the formation of Al–Mn–Fe intermetallic compounds (IMCs) has been investigated in the solidification of Mg–9Al-0.7Zn-0.2Mn (wt.%, AZ91) with iron contents ranging from ∼0.001 to > 0.01 wt.% Fe. Four Al–Mn–Fe IMCs formed depending on the Fe-content and location in the cruc...

Full description

Saved in:
Bibliographic Details
Published in:Intermetallics 2022-03, Vol.142, p.107465, Article 107465
Main Authors: Peng, L., Zeng, G., Xian, J., Gourlay, C.M.
Format: Article
Language:English
Subjects:
Aluminum
Automotive uses
Casting
Crucibles
Crystal structure
Electron backscatter diffraction
Intermetallic compounds
Intermetallic phases
Intermetallics
Iron
Magnesium base alloys
Manganese
Microstructure
Multiphase
Nucleation and growth
Orientation relationships
Solidification
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:The influence of iron on the formation of Al–Mn–Fe intermetallic compounds (IMCs) has been investigated in the solidification of Mg–9Al-0.7Zn-0.2Mn (wt.%, AZ91) with iron contents ranging from ∼0.001 to > 0.01 wt.% Fe. Four Al–Mn–Fe IMCs formed depending on the Fe-content and location in the crucible: B2–Al(Fe,Mn), Al8Mn5, Al11Mn4 and, at the bottom of crucibles, Al5Fe2. The four IMCs nucleated and grew on one another, producing multiphase particles. These usually contained numerous orientations that were all interrelated through simple orientation relationships that are discussed in terms of the similarities between the IMC crystal structures. The iron content affected the IMC phase fractions and the multiphase particle morphology. At low iron content, the Fe-rich B2 phase was encapsulated by a low-Fe Al8Mn5 shell. With increasing iron content, the Fe-rich phases (B2 and Al5Fe2) gradually became in direct contact with the α-Mg. The threshold Fe:Mn content for adequate corrosion performance is found to correlate approximately to where B2–Al(Fe,Mn) first becomes exposed to the α-Mg matrix. •Al–Mn–Fe IMCs nucleate on each other with interrelated orientation relationships.•Al8Mn5 and Al11Mn4 grow to fully or partially cover the Fe-rich B2–Al(Fe,Mn) core.•B2–Al(Fe,Mn) become in direct contact with α-Mg as Fe content increases.•Threshold Fe:Mn for corrosion correlates to B2–Al(Fe,Mn) becoming exposed to α-Mg.
ISSN:0966-9795
1879-0216
DOI:10.1016/j.intermet.2022.107465