Quantitative Characterization of the Interfacial Damage in EB-PVD Thermal Barrier Coating

Considering the influence of non-equibiaxial stress state and initial residual strain on the compressive buckling of the ceramic layer, a quantitative characterization method of the damage generated at the interface between the top coat and bond coat in thermal barrier coating based on uniaxial comp...

Full description

Saved in:
Bibliographic Details
Published in:Coatings (Basel) 2022-07, Vol.12 (7), p.984
Main Authors: Jing, Fulei, Yang, Junjie, Tang, Shibai, Wen, Quan, Zhang, Tao, Wu, Jian, Fan, Xueling
Format: Article
Language:English
Subjects:
Axial compression
Compression tests
Compressive properties
Cooling
Damage accumulation
Insulation
Mechanical properties
Oxidation
Protective coatings
Residual stress
Room temperature
Single crystals
Spallation
Strain
Temperature
Thermal analysis
Thermal barrier coatings
Thermal fatigue
Thickness
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Considering the influence of non-equibiaxial stress state and initial residual strain on the compressive buckling of the ceramic layer, a quantitative characterization method of the damage generated at the interface between the top coat and bond coat in thermal barrier coating based on uniaxial compression was developed. It was verified by the axial compression tests of the single crystal specimens with EB-PVD thermal barrier coating after undergoing various isothermal oxidation times and thermal cycles. On this basis, the correlations between the measured interfacial damage and the thermal loads experienced as well as the thickness of thermally grown oxide (TGO) were analyzed. The results show that the critical compressive strain inducing the spallation of thermal barrier coating at room temperature can effectively characterize the accumulation of interfacial damage caused by isothermal oxidation and thermal fatigue. Under the same TGO thickness, the damage caused by thermal fatigue is greater than that caused by isothermal oxidation. The total damage generated in thermal barrier coating can be divided into three parts: oxidatively driven damage related to TGO thickness, mechanically driven damage related to stress–strain cycles in the coating, and their interaction, where the interaction term is negative.
ISSN:2079-6412
2079-6412
DOI:10.3390/coatings12070984