Sensing the onset of epoxy coating degradation with combined Raman spectroscopy/atomic force microscopy/electrochemical impedance spectroscopy

The paper presents the results of investigation on epoxy resin durability upon 12-week exposure to UV radiation. The aim was early determination of the onset of epoxy degradation and for this purpose an epoxy film on steel substrate systems were periodically inspected using Raman spectroscopy, atomi...

Full description

Saved in:
Bibliographic Details
Published in:Progress in organic coatings 2023-01, Vol.174, p.107302, Article 107302
Main Authors: Szociński, M., Darowicki, K.
Format: Article
Language:English
Subjects:
AFM
Atomic force microscopy
Degradation
EIS
Electrochemical impedance spectroscopy
Epoxy coatings
Epoxy resin
Epoxy resins
Microscopy
Polymers
Raman spectroscopy
Spectrum analysis
Substrates
Topography
Ultraviolet radiation
UV degradation
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:The paper presents the results of investigation on epoxy resin durability upon 12-week exposure to UV radiation. The aim was early determination of the onset of epoxy degradation and for this purpose an epoxy film on steel substrate systems were periodically inspected using Raman spectroscopy, atomic force microscopy and electrochemical impedance spectroscopy. The behaviour of examined polymer could be divided into three periods: immunity, degradation initiation and failure. Early degradation initiation could be sensed only with Raman spectroscopy and AFM topography imaging where decrease in intensity of particular Raman peaks and discrete changes in topography constituted the fingerprints of UV-induced changes. At this stage electrochemical impedance spectroscopy and local dc current mapping with AFM did not provide any signs of forthcoming degradation since the epoxy film still exhibited sufficient barrier properties. Obtained results can be helpful in proper selection of investigation techniques in the situations where precise evaluation of polymer degradation onset is of key importance. •Evaluation of UV impact on epoxy film with combined Raman, AFM and EIS techniques•Revealed three stages of epoxy response: resistance, degradation initiation, failure•Identification of degradation initiation possible only with Raman and AFM topography•Degradation initiation does not alter barrier properties of the coating.•Failure in barrier properties identified with EIS and AFM local dc mapping
ISSN:0300-9440
1873-331X
DOI:10.1016/j.porgcoat.2022.107302