Moisture Ingress and Distribution in Bifacial Silicon Photovoltaics

Water participates in multiple modes of degradation in photovoltaic (PV) modules including encapsulant yellowing, delamination, and contact corrosion. To mitigate moisture-induced degradation, we must understand the kinetics of moisture in state-of-the-art encapsulants and module architectures. In t...

Full description

Saved in:
Bibliographic Details
Published in:IEEE journal of photovoltaics 2023-05, Vol.13 (3), p.365-372
Main Authors: Sidawi, Tala, Kumar, Rishi E., Slauch, Ian, Meier, Rico, Bertoni, Mariana I., Fenning, David P.
Format: Article
Language:English
Subjects:
Additives
Bifacial
Calibration
Degradation
durability
Encapsulation
Energy & Fuels
Ethylene vinyl acetates
Galvanic corrosion
Materials Science
modeling
Moisture
Moisture content
Moisture effects
Moisture measurement
Optical polymers
Optical variables measurement
Photovoltaic cells
photovoltaics (PVs)
Physics
Plastics
Polyolefins
Silicon
Water heating
Citations: Items that this one cites
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Water participates in multiple modes of degradation in photovoltaic (PV) modules including encapsulant yellowing, delamination, and contact corrosion. To mitigate moisture-induced degradation, we must understand the kinetics of moisture in state-of-the-art encapsulants and module architectures. In this article, we present a robust optical method to quantify water content in the front and rear side encapsulants of bifacial silicon PV modules, then use such measurements to validate a model for simulating water concentration in these modules. First, we quantify the solubility of water in four modern encapsulants: ethylene vinyl acetate and polyolefin, each with and without UV-blocking additives. Second, we use water reflectometry detection to measure the diffusion of moisture within glass-backsheet modules as a function of time and environmental condition. Third, we present a model of moisture transport in bifacial silicon PV modules and show it to be consistent with our measurements. Crucially, our methodology enables the separate evaluation of water content in the front encapsulant and the rear polymers within glass-backsheet modules. Overall, our work presents a quantitative picture of moisture in emerging module architectures and a framework to extend this approach other encapsulants and module designs.
ISSN:2156-3381
2156-3403
DOI:10.1109/JPHOTOV.2023.3243404