Quantifying the Impact of Al Deposition Method on Underlying Al2O3/Si Interface Quality

Oxide–semiconductor interface quality has often a direct impact on the electrical properties of devices and on their performance. Traditionally, the properties are characterized through metal–oxide–semiconductor (MOS) structures by depositing a metal layer and measuring the capacitance–voltage (C–V)...

Full description

Saved in:
Bibliographic Details
Published in:Physica status solidi. A, Applications and materials science Applications and materials science, 2023-10, Vol.220 (20)
Main Authors: Mack, Iris, Kawa Rosta, Quliyeva, Ulviyya, Ott, Jennifer, Pasanen, Toni P, Vähänissi, Ville, Zahra Sadat Jahanshah Rad, Juha-Pekka Lehtiö, Laukkanen, Pekka, Soldano, Caterina, Savin, Hele
Format: Article
Language:English
Subjects:
Aluminum oxide
Density
Deposition
Electrical properties
Evaporation
Impact damage
Magnetron sputtering
Metal oxide semiconductors
Metallizing
Silicon
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Oxide–semiconductor interface quality has often a direct impact on the electrical properties of devices and on their performance. Traditionally, the properties are characterized through metal–oxide–semiconductor (MOS) structures by depositing a metal layer and measuring the capacitance–voltage (C–V) characteristics. However, metal deposition process itself may have an impact on the oxide and the oxide–semiconductor interface. The impact of magnetron sputtering, e‐beam evaporation, and thermal evaporation on an Al2O3/Si interface is studied, where atomic layer deposited (ALD) Al2O3 is used, by MOS C–V and corona oxide characterization of semiconductors (COCOS) measurements. The latter allows characterization of the interface also in its original state before metallization. The results show that sputtering induces significant damage at the underlying Al2O3/Si interface as the measured interface defect density Dit increases from 1011 to 1013 cm−2 eV. Interestingly, sputtering also generates a high density of positive charges Qtot at the interface as the charge changes from −2×1012 to +7×1012 cm−2. Thermal evaporation is found to be a softer method, with modest impact on Dit and Qtot. Finally, Alnealing heals the damage but has also a significant impact on the charge of the film recovering the characteristic negative charge of Al2O3 (∼−4 × 1012 cm−2).
ISSN:1862-6300
1862-6319
DOI:10.1002/pssa.202200653