Effect of Sr on the microstructure and mechanical properties of hypereutectic Al-Si alloy

The hypereutectic aluminum silicon alloy (Si: 20wt.%) was modified by Al-10%Sr modifier. The results show that Sr has a significant refining effect on both primary and eutectic silicon in aluminum silicon alloy (Si: 20wt.%). When the additional amount of Sr reaches 0.4%, the grain size is refined fr...

Full description

Saved in:
Bibliographic Details
Published in:Journal of physics. Conference series 2024-01, Vol.2691 (1), p.012066
Main Authors: Teng, Hailin, Shi, Weixi, Zhou, Yi, Wang, Sihan, Wu, Fanjie, Na, Xiangyu, Li, Guimao, Hu, Yan
Format: Article
Language:English
Subjects:
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:The hypereutectic aluminum silicon alloy (Si: 20wt.%) was modified by Al-10%Sr modifier. The results show that Sr has a significant refining effect on both primary and eutectic silicon in aluminum silicon alloy (Si: 20wt.%). When the additional amount of Sr reaches 0.4%, the grain size is refined from 80-100 μm without modification to 30-50 μm after modification. The morphology of primary silicon has changed from a large plate-like shape to a deformed fine fishbone shape, while eutectic silicon has changed from a long needle shape to a point shape. The X-ray diffraction analysis results indicate that the Al2Si2Sr phase was generated in the modified alloy. The scanning electron microscopy analysis results show that after 0.4% Sr modification, a white triangular-shaped Al2Si2Sr phase appears in the aluminum silicon alloy (Si: 20wt.%) sample, which is the Al-Si-Sr ternary phase analyzed by XRD testing. The tensile testing results show that the Sr modification additional amount is 0.4%, and the tensile strength of aluminum silicon alloy (Si: 20wt.%) has been improved by about 11% from 162 MPa without modification to 200 MPa after modification.
ISSN:1742-6588
1742-6596
DOI:10.1088/1742-6596/2691/1/012066