Mechanical Properties Evaluation of Render Mortars with Different Waterproof Additive Compositions

• Published in: Key engineering materials 2021-03, Vol.880, p.161-167
• Main Authors: Galarza, Fernando Palacios, Rocha, Joaquin Humberto Aquino
• Format: Article
• Language: English
• Subjects: Additives; Admixtures; Bonding agents; Chemical composition; Compressive strength; Flexural strength; Mechanical properties
• ISSN: 1013-9826; 1662-9795; 1662-9795
• DOI: 10.4028/www.scientific.net/KEM.880.161

Waterproof additives and bonding agent mixtures are commonly employed in the setting up of render mortars. This practice often shows beneficial results, enhancing the properties of the common mortars. Yet, the use of these additives does not seem to have a direct effect on the mechanical properties of the mortars. This study thus aims to evaluate the influence of the use of waterproof and adhesion additives on the mechanical properties of render mortars. Based on their chemical composition, three different types of mortar admixtures were evaluated, using fourfold additive-mortar weight ratios: 0%, 1.5%, 3%, and 5%. Compressive and flexural strength tests were conducted after 28 days. The results showed a negative impact on the mechanical properties of the mortars. The lowest flexural and compression strength values reported are 1.52 and 4.57 (MPa), respectively. However, all compressive and flexural strength values lied within the limit range recommended by the “Mortars applied on walls and ceilings” construction code (i.e., ABNT NBR 13281). It is compulsory to continue the experimental tests to determine render mortars mechanical properties with higher waterproof additive-mortar weight ratios since higher ratios might produce mortars with non-allowed mechanical properties.