Synthesis of macroporous ZrO2–Al2O3 mixed oxides with mesoporous walls, using polystyrene spheres as template
Macroporous ZrO 2 –Al 2 O 3 mixed oxides with mesoporous walls were synthesized. The three-dimensional interconnected macroporous structures, of inorganic zirconia–alumina mixed oxides containing different alumina compositions (25, 50, 100 wt%), were prepared by sol–gel method from inorganic precurs...
Saved in:
Published in: | Journal of porous materials 2009-08, Vol.16 (4), p.473-479 |
---|---|
Main Authors: | , , |
Format: | Article |
Language: | English |
Subjects: | |
Citations: | Items that this one cites Items that cite this one |
Online Access: | Get full text |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | Macroporous ZrO
2
–Al
2
O
3
mixed oxides with mesoporous walls were synthesized. The three-dimensional interconnected macroporous structures, of inorganic zirconia–alumina mixed oxides containing different alumina compositions (25, 50, 100 wt%), were prepared by sol–gel method from inorganic precursors and using polystyrene microspheres with diameters of 685 and 1520 nm as templates. The final porous arrays with controllable pore size in the submicrometer range could be obtained by calcination of the organic template. The structural characteristics are discussed. The physicochemical characterization of the samples was carried out by N
2
physisorption (S
BET
), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The shrinkage of pore diameter was approximately 35%, and the wall thickness of inorganic framework varied between 135 and 154 nm. The specific surface areas, of the samples, were between 123 and 287 m
2
/g, obtaining the largest surface area with the highest alumina contents and the smallest templates. |
---|---|
ISSN: | 1380-2224 1573-4854 |
DOI: | 10.1007/s10934-008-9221-z |