Nano-indentation testing of new and fractured nickel-titanium endodontic instruments

• Published in: International endodontic journal 2012-05, Vol.45 (5), p.462-468
• Main Authors: Jamleh, A., Sadr, A., Nomura, N., Yahata, Y., Ebihara, A., Hanawa, T., Tagami, J., Suda, H.
• Format: Article
• Language: English
• Subjects: cyclic fatigue; Dental Alloys - chemistry; Dental Stress Analysis - instrumentation; Dentistry; Elastic Modulus; Equipment Design; Equipment Failure; Hardness; Humans; Materials Testing; nano-indentation; Nanotechnology; Nickel - chemistry; nickel-titanium instruments; Root Canal Preparation - instrumentation; Rotation; Stress, Mechanical; Surface Properties; Time Factors; Titanium - chemistry
• ISSN: 0143-2885; 1365-2591
• DOI: 10.1111/j.1365-2591.2011.01997.x

Jamleh A, Sadr A, Nomura N, Yahata Y, Ebihara A, Hanawa T, Tagami J, Suda H. Nano‐indentation testing of new and fractured nickel‐titanium endodontic instruments. International Endodontic Journal, 45, 462–468, 2012. Aim  To investigate the effect of cyclic fatigue on nickel‐titanium (NiTi) endodontic instruments using a nano‐indentation test. Methodology  Eight ProFile NiTi rotary instruments (size 30, taper 0.06; Dentsply Maillefer, Ballaigues, Switzerland) were tested using a cyclic fatigue set‐up until fracture. The fractured instruments and eight new NiTi instruments of the same size and taper were used for a nano‐indentation test on the internal surfaces of a NiTi instruments in the region just adjacent to their fractured edge (group I) and in the same region of the new group (group II), and the cutting part beside the shaft for both instruments [group III (fractured) and group IV (new)]. Data were statistically analyzed using one‐way analysis of variance and Games–Howell post hoc test. The alpha‐type error was set at 0.05. Results  Significant differences in terms of hardness and elastic modulus for each group (P