Synergistic flame retardant effect of metal hydroxide and nanoclay in EVA composites

This study focused on the flame retardancy of ethylene-vinyl acetate copolymer (EVA) in combination with metal hydroxide and nanoclay. Fire tests, such as limiting oxygen index (LOI), flammability (UL-94), cone calorimeter, and smoke density chamber were employed to evaluate the effect of compositio...

Full description

Saved in:
Bibliographic Details
Published in:Polymer degradation and stability 2012-06, Vol.97 (6), p.863-869
Main Authors: Yen, Ynh-Yue, Wang, Hsin-Ta, Guo, Wen-Jen
Format: Article
Language:English
Subjects:
aluminum hydroxide
Applied sciences
Blends
burning
calorimeters
Density
Ethylene vinyl acetates
ethylene-vinyl acetate
EVA
Exact sciences and technology
fire testing
Flame retardancy
flame retardants
flammability
heat
insulating materials
magnesium hydroxide
Metal hydroxide
Metal hydroxides
Nanoclay
nanoclays
Nanocomposites
Nanomaterials
Nanostructure
oxygen
Physicochemistry of polymers
Polymer industry, paints, wood
Smoke
synergism
Synergistic effect
Technology of polymers
thermal stability
thermogravimetry
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:This study focused on the flame retardancy of ethylene-vinyl acetate copolymer (EVA) in combination with metal hydroxide and nanoclay. Fire tests, such as limiting oxygen index (LOI), flammability (UL-94), cone calorimeter, and smoke density chamber were employed to evaluate the effect of composition variation for the metal hydroxide and the nanoclay in EVA composites. The experimental results showed that when the nanoclay of 1 or 2 weight per cent was substituted for the aluminum hydroxide or magnesium hydroxide in EVA blends, the LOI value was significantly improved while the V-0 rating was maintained. The data obtained from the cone calorimeter test indicated that the peak heat release rate (pk-HRR) is reduced by about 28%–47%. The smoke density data (maximal smoke density, Dm) showed a reduction by about 16%–25%. The thermogravimetric analysis (TGA) data also showed that the nanoclay increased the thermal stability and char residue of the EVA samples. Hence, it is suggested that the metal oxide layer on the burning surface is reinforced by the formation of silicate layer, which is both structured and compacted and acts as the insulation, and the newly formed layer responds to the synergistic effect of flame retardancy as well as smoke suppression observed in the EVA blends.
ISSN:0141-3910
1873-2321
DOI:10.1016/j.polymdegradstab.2012.03.043