Poly(ethyleneimine) nanofibrous affinity membrane fabricated via one step wet-electrospinning from poly(vinyl alcohol)-doped poly(ethyleneimine) solution system and its application

• Published in: Journal of membrane science 2011-09, Vol.379 (1), p.191-199
• Main Authors: Wang, Xuefen, Min, Minghua, Liu, Zongyuan, Yang, Yin, Zhou, Zhe, Zhu, Meifang, Chen, Yanmo, Hsiao, Benjamin S.
• Format: Article
• Language: English
• Subjects: absorption; adsorption; Affinity; alcohols; aqueous solutions; artificial membranes; cations; chelating agents; Chemistry; Colloidal state and disperse state; copper; crosslinking; EDTA (chelating agent); ethyleneimine; Exact sciences and technology; General and physical chemistry; glutaraldehyde; heavy metals; Membranes; Metal ions; Poly(ethyleneimine); Poly(vinylalcohol); polyvinyl alcohol; Surface physical chemistry; toxicity; wastewater; Wet-electrospinning
• ISSN: 0376-7388; 1873-3123
• DOI: 10.1016/j.memsci.2011.05.065

► Crosslinked poly(ethyleneimine) nanofibrous membranes were fabricated via wet-electrospinning. ► Poly(vinyl alcohol) was used as fiber-forming agent. ► The adsorbability for three heavy metal ions of PEI nanofibrous membranes was investigated. ► PEI nanofibrous membranes could be regenerated successfully in EDTA aqueous. Poly(ethyleneimine) (PEI) has high affinity for various metal ions and can be used as a chelating agent for the removal of heavy metal cations in wastewater. In this paper, we reported the successful fabrication of crosslinked PEI nanofibrous affinity membranes for removing heavy metal ions via wet-electrospinning from its aqueous solution with the aid of low loading fiber-forming agent poly(vinyl alcohol) (PVA). The coagulating bath for wet-electrospinning was composed of the crosslinking agent glutaraldehyde (GA) and N,N-dimethylformamide (DMF) as a non-solvent. The adsorbability for three heavy metal ions of the PEI nanofibrous affinity membrane doped with PVA was investigated in the aqueous solution. The results showed that the affinity of the membrane to three heavy metal ions was in the order of Cu(II) > Cd(II) > Pb(II), and the equilibrium absorption capacities for the three tested ions (all measured at 100 mg L −1 initial concentration) were 1.05 mmol g −1 (67.16 mg g −1), 1.04 mmol g −1 (116.94 mg g −1), and 0.43 mmol g −1 (90.03 mg g −1), respectively. The PEI nanofibrous affinity membrane adsorbed with heavy metal ions could be regenerated successfully in EDTA aqueous solution without significantly affecting its adsorption efficiency. This study extended the application scope of the PEI membrane for removing of the toxic heavy metal ions from the wastewater.