Some studies on evaluation of degradation in composite adhesive joints using ultrasonic techniques

► Oblique incidence ultrasonic inspection was carried out on CFRP-epoxy adhesive joints. ► Amplitude of reflection increased with degradation. ► A shift in the reflection minimum towards lower frequencies was observed in degraded samples. ► Analytical models showed a similar trend. ► The spectrum mi...

Full description

Saved in:
Bibliographic Details
Published in:Ultrasonics 2013-08, Vol.53 (6), p.1150-1162
Main Authors: Vijaya Kumar, R.L., Bhat, M.R., Murthy, C.R.L.
Format: Article
Language:English
Subjects:
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:► Oblique incidence ultrasonic inspection was carried out on CFRP-epoxy adhesive joints. ► Amplitude of reflection increased with degradation. ► A shift in the reflection minimum towards lower frequencies was observed in degraded samples. ► Analytical models showed a similar trend. ► The spectrum minimum shift was found to depend on interfacial stiffness of the joint. Experimental and theoretical studies on degradation of composite-epoxy adhesive joints were carried out on samples having different interfacial and cohesive properties. Oblique incidence ultrasonic inspection of bonded joints revealed that degradation in the adhesive can be measured by significant variation in reflection amplitude as also by a shift in the minima of reflection spectrum. It was observed that severe degradation of the adhesive leads to failure dominated by interfacial mode. Through this investigation it is demonstrated that a correlation exists between the bond strength and a frequency shift in reflection minimum. The experimental data was validated using analytical models. Though both bulk adhesive degradation and interfacial degradation influences the shift in spectrum minimum, the contribution of the latter was found to be significant. An inversion algorithm was used to determine the interfacial transverse stiffness using the experimental oblique reflection spectrum. The spectrum shift was found to depend on the value of interfacial transverse stiffness using which a qualitative assessment can be made on the integrity of the joint.
ISSN:0041-624X
1874-9968
DOI:10.1016/j.ultras.2013.01.014