Highly transparent and conductive Al-doped ZnO nanoparticulate thin films using direct write processing

• Published in: Nanotechnology 2014-05, Vol.25 (19), p.195301-9
• Main Authors: Vunnam, S, Ankireddy, K, Kellar, J, Cross, W
• Format: Article
• Language: English
• Subjects: Al-doped ZnO; Aluminum; Azo; Condensed matter: electronic structure, electrical, magnetic, and optical properties; Cracks; Deposition; direct write processing; electrical resistivity; Electrodes; Exact sciences and technology; Fullerenes and related materials; Nanostructure; Optical properties and condensed-matter spectroscopy and other interactions of matter with particles and radiation; optical transparency; Physics; Thin films; transparent conducting oxides; Visible and ultraviolet spectra; Zinc oxide
• ISSN: 0957-4484; 1361-6528
• DOI: 10.1088/0957-4484/25/19/195301

Solution processable Al-doped ZnO (AZO) thin films are attractive candidates for low cost transparent electrodes. We demonstrate here an optimized nanoparticulate ink for the fabrication of AZO thin films using scalable, low-cost direct write processing (ultrasonic spray deposition) in air at atmospheric pressure. The thin films were made via thermal processing of as-deposited films. AZO films deposited using the proposed nanoparticulate ink with further reducing in vacuum and rf plasma of forming gas exhibited optical transparency greater than 95% across the visible spectrum, and electrical resistivity of 0.5 cm and it drops down to 7.0 × 10−2 cm after illuminating with UV light, which is comparable to commercially available tin doped indium oxide colloidal coatings. Various structural analyses were performed to investigate the influence of ink chemistry, deposition parameters, and annealing temperatures on the structural, optical, and electrical characteristics of the spray deposited AZO thin films. Optical micrographs confirmed the presence of surface defects and cracks using the AZO NPs ink without any additives. After adding N-(2-Aminoethyl)-3-aminopropylmethyldimethoxy silane to the ink, AZO films exhibited an optical transparency which was virtually identical to that of the plain glass substrate.