Finite element modeling of multilayered structures of fish scales

• Published in: Journal of the mechanical behavior of biomedical materials 2014-12, Vol.40, p.375-389
• Main Authors: Chandler, Mei Qiang, Allison, Paul G, Rodriguez, Rogie I, Moser, Robert D, Kennedy, Alan J
• Format: Article
• Language: English
• Subjects: Animals; Cracking (fracturing); Finite Element Analysis; Finite element method; Fish; Fishes; Flakes (defects); Fracture mechanics; Mathematical analysis; Models, Biological; Skin - chemistry; Spatulas; Strength; Stress, Mechanical
• ISSN: 1751-6161; 1878-0180
• DOI: 10.1016/j.jmbbm.2014.09.013

The interlinked fish scales of Atractosteus spatula (alligator gar) and Polypterus senegalus (gray and albino bichir) are effective multilayered armor systems for protecting fish from threats such as aggressive conspecific interactions or predation. Both types of fish scales have multi-layered structures with a harder and stiffer outer layer, and softer and more compliant inner layers. However, there are differences in relative layer thickness, property mismatch between layers, the property gradations and nanostructures in each layer. The fracture paths and patterns of both scales under microindentation loads were different. In this work, finite element models of fish scales of A. spatula and P. senegalus were built to investigate the mechanics of their multi-layered structures under penetration loads. The models simulate a rigid microindenter penetrating the fish scales quasi-statically to understand the observed experimental results. Study results indicate that the different fracture patterns and crack paths observed in the experiments were related to the different stress fields caused by the differences in layer thickness, and spatial distribution of the elastic and plastic properties in the layers, and the differences in interface properties. The parametric studies and experimental results suggest that smaller fish such as P. senegalus may have adopted a thinner outer layer for light-weighting and improved mobility, and meanwhile adopted higher strength and higher modulus at the outer layer, and stronger interface properties to prevent ring cracking and interface cracking, and larger fish such as A. spatula and Arapaima gigas have lower strength and lower modulus at the outer layers and weaker interface properties, but have adopted thicker outer layers to provide adequate protection against ring cracking and interface cracking, possibly because weight is less of a concern relative to the smaller fish such as P. senegalus.