Development and testing of an intermediate temperature glass sealant for use in mixed ionic and electronic conducting membrane reactors

• Published in: Solid state ionics 2010-06, Vol.181 (15), p.767-774
• Main Authors: Hatcher, Joanne, Pascual, María Jesús, Poulidi, Danai, Metcalfe, Ian S.
• Format: Article
• Language: English
• Subjects: Borosilicate glasses; Ceramics; Cooling rate; Electrochemical promotion; Glass sealants; Heating; Leaks; Membranes; MIEC membranes; Reactors; Sealers; Sealing; Seals
• ISSN: 0167-2738; 1872-7689
• DOI: 10.1016/j.ssi.2010.03.031

High temperature ceramic membranes have interesting possibilities for application in areas of new and developing technologies such as hydrocarbon combustion with carbon dioxide capture and electrochemical promotion of catalysis (EPOC). However, membrane module sealing remains a significant technical challenge. In this work a borosilicate glass sealant (50SiO 2·25B 2O 3·25Na 2O, mol%) was developed to fit the requirements of sealing an air separation membrane system at intermediate temperatures (300–600 °C). The seal was assessed by testing the leak rates under a range of conditions. The parameters tested included the effect of flowrate on the leak rate, the heating and cooling rates of the reactor and the range of temperatures under which the system could operate. Tests for durability and reliability were also performed. It was found that the most favourable reactor configuration employed a reactor with the ceramic pellet placed underneath the inner chamber alumina tube (inverted configuration), using a quartz wool support to keep the membrane in place prior to sealing. Using this configuration the new glass-based seal was found to be a more suitable sealant than traditional alternatives; it produced lower leak rates at all desirable flowrates, with the potential for rapid heating and cooling and multiple cycling, allowing for prolonged usage.