Graphitic carbon nanofibers developed from bundles of aligned electrospun polyacrylonitrile nanofibers containing phosphoric acid

Graphitic carbon nanofibers (GCNFs) with diameters of approximately 300 nm were developed using bundles of aligned electrospun polyacrylonitrile (PAN) nanofibers containing phosphoric acid (PA) as the innovative precursors through thermal treatments of stabilization, carbonization, and graphitizatio...

Full description

Saved in:
Bibliographic Details
Published in:Polymer (Guilford) 2010-05, Vol.51 (11), p.2360-2367
Main Authors: Zhou, Zhengping, Liu, Kunming, Lai, Chuilin, Zhang, Lifeng, Li, Juanhua, Hou, Haoqing, Reneker, Darrell H., Fong, Hao
Format: Article
Language:English
Subjects:
Applied sciences
Bundles
Carbon fibers
Carbonization
Electrospinning
Exact sciences and technology
Fibers and threads
Forms of application and semi-finished materials
Graphitic carbon nanofibers
Nanofibers
Phosphoric acid
Polyacrylonitrile
Polyacrylonitriles
Polymer industry, paints, wood
Precursors
Stabilization
Technology of polymers
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Graphitic carbon nanofibers (GCNFs) with diameters of approximately 300 nm were developed using bundles of aligned electrospun polyacrylonitrile (PAN) nanofibers containing phosphoric acid (PA) as the innovative precursors through thermal treatments of stabilization, carbonization, and graphitization. The morphological, structural, and mechanical properties of GCNFs were systematically characterized and/or evaluated. The GCNFs made from the electrospun PAN precursor nanofibers containing 1.5 wt.% of PA exhibited mechanical strength that was 62.3% higher than that of the GCNFs made from the precursor nanofibers without PA. The molecules of PA in the electrospun PAN precursor nanofibers initiated the cyclization and induced the aromatization during stabilization, as indicated by the FT-IR and TGA results. The stabilized PAN nanofibers possessed regularly oriented ladder structures, which facilitated the further formation of ordered graphitic structures in GCNFs during carbonization and graphitization, as indicated by the TEM, XRD, and Raman results. [Display omitted]
ISSN:0032-3861
1873-2291
DOI:10.1016/j.polymer.2010.03.044