Depth dependent order/disorder transitions in iron-rich thin films grown on i-Al–Pd–Mn studied by medium energy ion scattering

• Published in: Surface science 2014-02, Vol.620, p.59-64
• Main Authors: Noakes, T.C.Q., Parle, J., Nugent, P., Sharma, H.R., Smerdon, J.A., Bailey, P., McGrath, R.
• Format: Article
• Language: English
• Subjects: Aluminum; Condensed matter: electronic structure, electrical, magnetic, and optical properties; Condensed matter: structure, mechanical and thermal properties; Cross-disciplinary physics: materials science; rheology; Deposition; Disorders; Epitaxy; Exact sciences and technology; Ferrous alloys; Intermetallic compounds; Intermetallics; Ion scattering; Iron; Iron aluminides; MEIS; Physics; Quasicrystals; Thin films
• ISSN: 0039-6028; 1879-2758
• DOI: 10.1016/j.susc.2013.09.023

This paper reports a medium energy ion scattering study of the room temperature deposition of Fe on the five-fold surface of i-Al70Pd21Mn9. At low coverage (~1 ML) growth results in a disordered alloy film with significant Al content. At higher coverage (~11 ML) again an alloy film is formed, but this time with an average composition that slowly varies through the film but is close to stoichiometric Fe3Al. This composition is consistent with magnetic ordering which has been observed in previous experiments on this system. Structural analysis indicates five domains of bcc-like structure in the film, which is oriented with (110) type planes parallel to the five-fold quasicrystal surface. There is a distinct structural transition within the film between a compressed layer near the surface and a slightly expanded layer directly above the quasicrystalline substrate. The sub-surface layer has considerable disorder and the change in layer spacing is attributed to this order/disorder transition within the film. Annealing to 300°C for 10min induces a small amount of further up-diffusion of Al into the film and also some segregation of Al to the surface, although structurally the film remains essentially unchanged, with the order/disorder transition occurring at a similar depth. •This paper reports a MEIS study of the RT deposition of Fe onto 5f i-Al70Pd21Mn9•~1 ML, disordered alloy film with significant Al content from up-diffusion•~11 ML, close to Fe3Al, bcc-like structure with a distinct depth-dependent transition•Compressed layer near the surface, expanded and disordered layer above the substrate•Annealing to 300ºC for 10min the film remains structurally unchanged.