Sintering mechanisms of Yttria with different additives
The sintering behaviour of conventional yttria powder was investigated, with emphasis on the effect of sintering additives such as B2O3, YF3, Al2O3, ZrO2, and TiO2, etc. at sintering temperatures from 1000°C to 1600°C. Powder shrinkage behaviour was analysed using a dilatometer. The powder sintering...
Saved in:
Published in: | Ceramics international 2013-07, Vol.39 (5), p.4791-4799 |
---|---|
Main Authors: | , , , |
Format: | Article |
Language: | English |
Subjects: | |
Citations: | Items that this one cites Items that cite this one |
Online Access: | Get full text |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | The sintering behaviour of conventional yttria powder was investigated, with emphasis on the effect of sintering additives such as B2O3, YF3, Al2O3, ZrO2, and TiO2, etc. at sintering temperatures from 1000°C to 1600°C. Powder shrinkage behaviour was analysed using a dilatometer. The powder sintering mechanisms were identified at different temperatures using powder isothermal shrinkage curves. This analysis showed that the sintering additives B2O3 and YF3 could improve yttria sintering by changing the diffusion/sintering mechanisms at certain temperatures, while sintering additives TiO2, Al2O3 and ZrO2 appeared to retard the powder densification at temperatures around 1000°C and are more suitable when used at temperatures in excess of 1300°C. The powder with La2O3 added had the slowest densification rate throughout the test temperatures in this experiment and was also found to be more suitable when used at temperatures higher than 1550°C. |
---|---|