Effects of AlPO4 addition on the corrosion resistance of andalusite-based low-cement castables with molten Al-alloy

This paper investigates the effects of AlPO4 addition on the corrosion resistance of andalusite LCC refractories. Corrosion tests using the Alcoa cup test (850°C and 1160°C for 150h and 72h, respectively) were conducted to determine the extent of penetration. The addition of AlPO4 was shown to impro...

Full description

Saved in:
Bibliographic Details
Published in:Journal of the European Ceramic Society 2013-06, Vol.33 (6), p.1067-1075
Main Authors: AdabiFiroozjaei, Esmaeil, Koshy, Pramod, Sorrell, Charles Christopher
Format: Article
Language:English
Subjects:
AlPO4
Aluminum
Andalusite LCC refractories
Castable refractories
Corrosion resistance
Corundum
Dissolution
Interface reactions
Interfacial reaction
Phosphorus
Phosphorus trioxide gas
Ultrasonic testing
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:This paper investigates the effects of AlPO4 addition on the corrosion resistance of andalusite LCC refractories. Corrosion tests using the Alcoa cup test (850°C and 1160°C for 150h and 72h, respectively) were conducted to determine the extent of penetration. The addition of AlPO4 was shown to improve the corrosion resistance of the castables in contact with molten Al-alloy. SEM/EDS analyses of the interfacial reaction zone showed the formation of corundum in the interfacial layer, along with a significant decrease in the phosphorus content in the interface. Thermodynamic calculations revealed that reaction with the alloy leads to the formation of corundum as the reaction product along with gaseous products (phosphorus trioxide gas) and small amounts of aluminum phosphide. Corundum formation at the interface enhances the corrosion resistance of sample due to high stability of corundum against molten Al alloy, while the metal quality is enhanced due to absence of dissolved phosphorus in the metal.
ISSN:0955-2219
1873-619X
DOI:10.1016/j.jeurceramsoc.2012.11.005