Femtosecond Nanostructuring of Glass with Optically Trapped Microspheres and Chemical Etching

• Published in: ACS applied materials & interfaces 2015-12, Vol.7 (49), p.27467-27472
• Main Authors: Shakhov, A, Astafiev, A, Gulin, A, Nadtochenko, V
• Format: Article
• Language: English
• ISSN: 1944-8244; 1944-8252
• DOI: 10.1021/acsami.5b09454

Laser processing with optically trapped microspheres is a promising tool for nanopatterning at subdiffraction-limited resolution in a wide range of technological and biomedical applications. In this paper, we investigate subdiffraction-limited structuring of borosilicate glass with femtosecond pulses in the near-field of optically trapped microspheres combined with chemical postprocessing. The glass surface was processed by single laser pulses at 780 nm focused by silica microspheres and then subjected to selective etching in KOH, which produced pits in the laser-affected zones (LAZs). Chemical postprocessing allowed obtaining structures with better resolution and reproducibility. We demonstrate production of reproducible pits with diameters as small as 70 nm (λ/11). Complex two-dimensional structures with 100 nm (λ/8) resolution were written on the glass surface point by point with microspheres manipulated by optical tweezers. Furthermore, the mechanism of laser modification underlying selective etching was investigated with mass spectrum analysis. We propose that the increased etching rate of laser-treated glass results from changes in its chemical composition and oxygen deficiency.