Size dependence of the trapped magnetic field in large single-grained Gd-Ba-Cu-O bulk superconductors

Based on careful consideration to crystal growth mechanism, three different sizes of Gd-Ba-Cu-O cylindrical bulk superconductors have been fabricated. The trapped magnetic field proportionally increased with the sample size and the peak heights at 77 K were 0.91-0.95 T, 1.38-1.51 T and 1.91-2.03 T f...

Full description

Saved in:
Bibliographic Details
Published in:Journal of physics. Conference series 2014-05, Vol.507 (1), p.12048-4
Main Authors: Teshima, H, Morita, M
Format: Article
Language:English
Subjects:
CRYSTAL GROWTH
Gadolinium
Liners
MAGNETIC FIELD
Magnetic fields
Physics
SUPERCONDUCTORS
Trapped magnetic fields
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Based on careful consideration to crystal growth mechanism, three different sizes of Gd-Ba-Cu-O cylindrical bulk superconductors have been fabricated. The trapped magnetic field proportionally increased with the sample size and the peak heights at 77 K were 0.91-0.95 T, 1.38-1.51 T and 1.91-2.03 T for samples 30 mm, 46 mm and 64.5 mm in diameter, respectively. In addition, macroscopic Jc of approximately 13,000 A/cm2 was estimated for all samples with different sizes. Such a high value of macroscopic Jc and the liner increase of trapped fields with size can be ascribed to excellent quality of large single-grained Gd-Ba-Cu-O bulk superconductors.
ISSN:1742-6596
1742-6588
1742-6596
DOI:10.1088/1742-6596/507/1/012048