Water-soluble luminescent‐electrical‐magnetic trifunctional composite nanofibers prepared via electrospinning technique

Water-soluble PF-Na/Fe3O4/PVA luminescent–electrical–magnetic trifunctional composite nanofibers were successfully fabricated by electrospinning. It was found that the average diameter of as-prepared composite nanofibers was 204nm. The samples emitted a bright blue fluorescence under UV–illumination...

Full description

Saved in:
Bibliographic Details
Published in:Materials letters 2015-11, Vol.159, p.159-162
Main Authors: Guo, Dechao, Sun, Zhiyao, Xu, Laidi, Gao, Yang, Dai, Mingming, Wang, Shuhong, Chang, Qing, Wang, Cheng, Ma, Dongge
Format: Article
Language:English
Subjects:
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Water-soluble PF-Na/Fe3O4/PVA luminescent–electrical–magnetic trifunctional composite nanofibers were successfully fabricated by electrospinning. It was found that the average diameter of as-prepared composite nanofibers was 204nm. The samples emitted a bright blue fluorescence under UV–illumination and the maximum excitation and emission wavelengths of photoluminescence for the composite nanofibers were about 350nm and 416nm, respectively. Magnetic hysteresis loops confirmed that the composite nanofibers possess superparamagnetic properties and showed a high saturated magnetization (Ms=9.7emµ/g) at room temperature. The composite nanofibers exhibited excellent luminescent, electrical and magnetic properties. In addition, they have good biocompatibility and low toxicity. The luminescent–electrical–magnetic trifunctional composite nanofibers have great potential in the biomedical field applications and photoelectric devices. One-dimensional luminescent–electrical–magnetic trifunctional composite nanofibers were prepared by electrospinning. The composite nanofibers have excellent optical, electrical and magnetic characterization, which can be tuned by adding different concentration of PF-Na and Fe3O4 NPs into them, respectively. [Display omitted] •One-dimensional luminescent–electrical–magnetic composite nanofibers were prapared.•All of the raw materials are water-soluble, without pollution and low toxicity.•The TEM images demonstrated that the composite nanofibers are smooth and continuous.•The Fe3O4 NPs with uniform dispersion in the composite nanofibers were observed.•The optical, electrical and magnetic characterization can be tuned freely.