A highly anticorrosive chromium-free conversion coating prepared on electroless Ni–P coating

Two kinds of chromium-free conversion coatings, including manganate conversion coating (MCC) and manganate/silicate composite conversion coating (MSCC), were prepared on electroless Ni–P coatings (ENPC) to improve the anticorrosive property of ENPC instead of chromate conversion coating (CCC). The E...

Full description

Saved in:
Bibliographic Details
Published in:Surface & coatings technology 2016-02, Vol.287, p.25-32
Main Authors: Gan, Yiwei, Chen, Dexin, Kang, Zhixin
Format: Article
Language:English
Subjects:
Chromium-free conversion coating
Conversion coating
Corrosion
Corrosion prevention
Corrosion resistance
EIS
Electroless coatings
Electroless Ni–P coating
Manganates
Nickel
Polarization
XPS
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Two kinds of chromium-free conversion coatings, including manganate conversion coating (MCC) and manganate/silicate composite conversion coating (MSCC), were prepared on electroless Ni–P coatings (ENPC) to improve the anticorrosive property of ENPC instead of chromate conversion coating (CCC). The EDX and XPS analyses illustrated the chemical compositions of MCC and MSCC mainly contained Ni(OH)2, NiO and MnO2, which acted as a physical barrier to inhibit the transfer of the charges and the movement of the ions in corrosion process. Compared with the MCC, an additional layer of polymeric silicate was formed on the surface of MSCC, which leaded to better corrosion resistance. In potentiodynamic polarization test, the MSCC showed the lowest corrosion current density (icorr) with value of 0.050μA/cm2, which decreased by around two orders of magnitude compared with untreated ENPC. Moreover, the polarization resistance (Rp) of MSCC was about 7 times higher than that of CCC. The fitting parameters of EIS explained the reason why the MSCC exhibited better anticorrosive performance than the MCC. The result of neutral salt spray test (NSS) intuitively proved that the MSCC can replace the CCC to improve the anticorrosive property of ENPC. •Manganate conversion coating (MCC) was prepared on Ni–P coating.•Manganate/silicate conversion coating (MSCC) was prepared on Ni–P coating.•MSCC exhibited better anticorrosive property than MCC.•Corrosion resistance of MSCC was much higher than chromate conversion coating.
ISSN:0257-8972
1879-3347
DOI:10.1016/j.surfcoat.2015.12.080