Significance and interaction of bonding parameters with bonding ratio in press bonding of TC4 alloy

The variation of bonding ratio in the press bonding of TC4 alloy at temperatures from 850 to 900℃,pressures from 10 to 30 MPa,and time from 5 to 15 min was investigated.The bonding ratio increases with the increase of temperature,time and pressure.The maximum bonding ratio,i.e.98 %,can be obtained a...

Full description

Saved in:
Bibliographic Details
Published in:Rare metals 2016-03, Vol.35 (3), p.235-241
Main Authors: Li, Hong, Li, Miao-Quan, Yu, Wei-Xin, Liu, Hong-Bin
Format: Article
Language:English
Subjects:
Biomaterials
Bonding
Chemistry and Materials Science
Energy
Materials Engineering
Materials Science
Metallic Materials
Nanoscale Science and Technology
Physical Chemistry
Presses
TC4钛合金
加压力
参数范围
工艺参数
温度
粘接
结合率
键合
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:The variation of bonding ratio in the press bonding of TC4 alloy at temperatures from 850 to 900℃,pressures from 10 to 30 MPa,and time from 5 to 15 min was investigated.The bonding ratio increases with the increase of temperature,time and pressure.The maximum bonding ratio,i.e.98 %,can be obtained at 900℃,30 MPa and 15 min.The significance and interaction of bonding parameters with the bonding ratio were investigated.The results demonstrate that the effect of pressure on the bonding ratio is the most effective and the effect of temperature is secondary,while the effect of time is not very powerful.The interaction of bonding parameter on the bonding ratio exists but that is distinguishing in different bonding parameter ranges.It is concluded that increasing pressure can be considered as the primary method to increase the bonding ratio.
ISSN:1001-0521
1867-7185
DOI:10.1007/s12598-014-0330-3