Effect of Argon Addition on Morphology and Structure of Diamond Films (from Microcrystalline to Nanocrystalline)

Micro-/nanocrystalline diamond films deposited in Ar/H sub(2)/CH sub(4) microwave plasmas have been studied, with argon flow rates in the range of 70-100 sccm. The effects of argon addition on morphology, surface roughness, quality and structure were investigated by scanning electron microscopy, sur...

Full description

Saved in:
Bibliographic Details
Published in:Plasma science & technology 2015-03, Vol.17 (3), p.216-220
Main Authors: LV, Lin, WANG, Jianhua, WENG, Jun, CUI, Xiaohui, ZHANG, Ying
Format: Article
Language:English
Subjects:
Argon
Crystallography
Diamond films
Flow rate
Morphology
Nanocrystals
Planes
Surface roughness
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Micro-/nanocrystalline diamond films deposited in Ar/H sub(2)/CH sub(4) microwave plasmas have been studied, with argon flow rates in the range of 70-100 sccm. The effects of argon addition on morphology, surface roughness, quality and structure were investigated by scanning electron microscopy, surface profiler, Raman spectrometer and X-ray diffraction (XRD). It is demonstrated that when the argon flow rate is 70 sccm or 75 sccm, well-faceted polycrystalline diamond films can be grown at a low substrate temperature less than 610 degree C. With the increase in the argon flow rate, the smooth crystallographic planes disappear gradually. Instead, rough crystallographic planes made up of small aggregates begin to take shape, resulting from the increase in the secondary nucleation rate. Nanocrystalline diamond films were obtained at a flow rate of 100 sccm, and all of the prepared diamond films were smooth, with a surface roughness (Ra) less than 20 nm. Raman analyses reveal that the amount of amorphous carbon increases significantly with the increase in argon flow. The results of XRD show that crystalline size and preferential orientation of diamond films depend on the argon content in the plasmas.
ISSN:1009-0630
DOI:10.1088/1009-0630/17/3/08