Silica encapsulation by miniemulsion polymerization: A novel approach of efficient chemical functionalization on silica nanoparticles

Hybrid latex particles with core-shell nanostructure were prepared via miniemulsion polymerization. Copolymer of (methyl methacrylate-butyl acrylate-methacrylic acid) was formed the shell on the surface of modified SiO2 nanoparticles as the core. In order to create compatibility between inorganic an...

Full description

Saved in:
Bibliographic Details
Published in:Polymer (Guilford) 2016-08, Vol.98, p.182-189
Main Authors: mirmohseni, Abdolreza, Gharieh, Ali, Khorasani, Manouchehr
Format: Article
Language:English
Subjects:
Acrylic
Copolymers
Encapsulation
Latex
Miniemulsion polymerization
Modified SiO2
Nanocomposite
Nanocomposites
Nanoparticles
Phases
Polymerization
Silicon dioxide
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Hybrid latex particles with core-shell nanostructure were prepared via miniemulsion polymerization. Copolymer of (methyl methacrylate-butyl acrylate-methacrylic acid) was formed the shell on the surface of modified SiO2 nanoparticles as the core. In order to create compatibility between inorganic and polymeric phases, modification of SiO2 nanoparticles was performed with methylene diphenyl diisocyanate and 2-hydroxy ethyl methacrylate with an optimized procedure for the first time, and then miniemulsion polymerization was carried out in the presence of modified SiO2. The products of each step were characterized. The results of DLS, TEM and SEM analyses proved the formation of encapsulated hybrid latex particles. DLS and SEM data revealed that the sizes of nanocomposite particles vary between 60 and 120 nm for 0–10 wt% of the modified SiO2 nanoparticles. Thermal stability and thermo-mechanical properties of the obtained nanocomposite films were studied by TGA and DMTA, respectively. It was found that the best improvement of properties is achieved for nanocomposite containing 7 wt% modified silica nanoparticles. [Display omitted] •A new, efficient and cost effective two-step surface modification of silica nanoparticles was developed.•Latexes with different amount of highly dispersed modified particles obtained via miniemulsion polymerization.•The dried film of nanocomposite latexes showed superior thermal stability and thermo-mechanical properties.
ISSN:0032-3861
1873-2291
DOI:10.1016/j.polymer.2016.06.033