Two-step synthesis of binary Ni–Fe sulfides supported on nickel foam as highly efficient electrocatalysts for the oxygen evolution reaction

A facile two-step method has been used to synthesize binary Ni-Fe sulfides supported on nickel foam (NF) as electrocatalysts for the oxygen evolution reaction (OER). Firstly, NiFe hydroxide nanosheets have been electrodeposited on NF (NiFe/NF) as a precursor with a large surface area. Secondly, the...

Full description

Saved in:
Bibliographic Details
Published in:Journal of materials chemistry. A, Materials for energy and sustainability Materials for energy and sustainability, 2016-01, Vol.4 (35), p.13499-13508
Main Authors: Dong, Bin, Zhao, Xin, Han, Guan-Qun, Li, Xiao, Shang, Xiao, Liu, Yan-Ru, Hu, Wen-Hui, Chai, Yong-Ming, Zhao, Hui, Liu, Chen-Guang
Format: Article
Language:English
Subjects:
Electrocatalysts
Intermetallics
Iron compounds
Nickel
Nickel base alloys
Nickel compounds
Stability
Sulfides
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:A facile two-step method has been used to synthesize binary Ni-Fe sulfides supported on nickel foam (NF) as electrocatalysts for the oxygen evolution reaction (OER). Firstly, NiFe hydroxide nanosheets have been electrodeposited on NF (NiFe/NF) as a precursor with a large surface area. Secondly, the as-prepared NiFe/NF has been subjected to a hydrothermal sulfuration process in order to prepare NiFeS/NF as an efficient electrocatalyst for the OER. The as-prepared samples have been characterized by XRD, XPS and SEM. The SEM images show that the NiFeS film was composed of needle-like nanostructures covering the surface of the NF. The corresponding OER performances in alkaline media have been systematically investigated. NiFeS/NF shows a superior overpotential of 65 mV at 10 mA cm-2, which is much lower than most Ni-based electrocatalysts. The overpotential of 189 mV at 100 mA cm-2 of NiFeS/NF suggests very promising OER activity for industrial applications. The electrochemically active surface area (251.25 cm2) of NiFeS/NF is obviously larger than that of NiFeS/NF (173.75 cm2) and NiFeS/NF (205.00 cm2). However, the stability of NiFeS/NF is not very good due to the intrinsic nature of metal sulfides in alkaline solution. An approach of electrodeposition of Fe hydroxide film on NiFeS/NF (NiFeS-Fe/NF) has been used to protect NiFeS/NF for better stability for the OER. The OER performances of NiFeS-Fe/NF demonstrate enhanced stability but lower activity with 101.6 mV at 10 mA cm-2. Therefore, there may be an optimal balance between activity and stability of transition metal sulfides for the OER.