Mechanical and oxidation properties of C/SiC corrugated lattice core composite sandwich panels

Carbon fiber reinforced silicon carbide (C/SiC) corrugated lattice core composite sandwich structures were fabricated by precursor infiltration and pyrolysis (PIP) with polycarbosilane as the matrix precursor, and effects of high-temperature oxidation on the microstructures and mechanical properties...

Full description

Saved in:
Bibliographic Details
Published in:Composite structures 2016-12, Vol.158, p.137-143
Main Authors: Yang, Fan, Cheng, Su, Zeng, Tao, Wang, Zhi-hai, Xu, Guo-dong, Zhai, Jun-jun, Fang, Dai-ning
Format: Article
Language:English
Subjects:
C/SiC
Compressive strength
Corrugating
Lattice sandwich
Lattices
Mechanical properties
Oxidation
Precursor infiltration and pyrolysis
Precursors
Sandwich structures
Silicon carbide
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Carbon fiber reinforced silicon carbide (C/SiC) corrugated lattice core composite sandwich structures were fabricated by precursor infiltration and pyrolysis (PIP) with polycarbosilane as the matrix precursor, and effects of high-temperature oxidation on the microstructures and mechanical properties of C/SiC composite sandwich structures were investigated. It was found that the high-temperature oxidation had a great effect on the mechanical properties of C/SiC composite sandwich structures. When the oxidation time was 30min, the compression strength of C/SiC composite sandwich structures first decreased and then increased with the elevation of oxidation temperature controlled by two competition mechanisms. The compression modulus changed slightly. Different fracture behaviors were shown after oxidation at 1200°C and 1600°C. The compression strength and modulus of C/SiC composite sandwich structures after oxidation at 1600°C decreased with oxidation time. The brittle fracture behavior appeared after 60min oxidation.
ISSN:0263-8223
1879-1085
DOI:10.1016/j.compstruct.2016.09.034