Multiple Structural Transitions in Langmuir Monolayers of Charged Soft-Shell Nanoparticles

• Published in: Langmuir 2018-04, Vol.34 (13), p.3909-3917
• Main Authors: El-Tawargy, A. S, Stock, D, Gallei, M, Ramadan, W. A, Shams El-Din, M. A, Reiter, G, Reiter, R
• Format: Article
• Language: English
• ISSN: 0743-7463; 1520-5827
• DOI: 10.1021/acs.langmuir.7b03656

We have investigated the morphologies of Langmuir layers of charged, polymeric hard-core/interlayer/soft-shell nanoparticles spread at the air–water interface. Depending on various mutual interactions, which are correlated to the areal densities of the deposited nanoparticles, we observed ordered patterns of nondense and closed-packed arrangements of core/interlayer/shell (CIS) nanoparticle ordering. At low areal densities, we found an almost regular distribution of the charged CIS nanoparticles on the water surface, which resulted from long-range repulsive electrostatic interactions between them. At higher areal densities, domains of more closely packed and ordered nanoparticles were formed, coexisting with regions of randomly and sparsely distributed nanoparticles. We relate these domains to the interplay of electrostatic repulsion and capillary attraction caused by the dipolar character of like-charged particles at the interface, allowing for a characteristic separation distance between nanoparticles of about 3–4 times the nanoparticle diameter. At relatively high areal densities, attractive van der Waals forces were finally capable of making nanoparticles to come in contact with each other, leading to densely packed patches of hexagonally ordered nanoparticles coexisting with regions of rather well-ordered nanoparticles separated by about 1 μm and regions of randomly and sparsely distributed nanoparticles. Intriguingly, upon re-expansion of the area available per nanoparticle, these densely packed patches disappeared, indicating that steric repulsion due to the presence of soft shells as well as long-range electrostatic repulsive forces were strong enough to assure reversibility of the morphological behavior.