Boosting the Recoverable Energy Density of Lead-Free Ferroelectric Ceramic Thick Films through Artificially Induced Quasi-Relaxor Behavior

• Published in: ACS applied materials & interfaces 2018-06, Vol.10 (24), p.20720-20727
• Main Authors: Peddigari, Mahesh, Palneedi, Haribabu, Hwang, Geon-Tae, Lim, Kyung Won, Kim, Ga-Yeon, Jeong, Dae-Yong, Ryu, Jungho
• Format: Article
• Language: English
• ISSN: 1944-8244; 1944-8252
• DOI: 10.1021/acsami.8b05347

Dielectric ceramic film capacitors, which store energy in the form of electric polarization, are promising for miniature pulsed power electronic device applications. For a superior energy storage performance of the capacitors, large recoverable energy density, along with high efficiency, high power density, fast charge/discharge rate, and good thermal/fatigue stability, is desired. Herein, we present highly dense lead-free 0.942­[Na0.535K0.480NbO3]–0.058LiNbO3 (KNNLN) ferroelectric ceramic thick films (∼5 μm) demonstrating remarkable energy storage performance. The nanocrystalline KNNLN thick film fabricated by aerosol deposition (AD) process and annealed at 600 °C displayed a quasi-relaxor ferroelectric behavior, which is in contrast to the typical ferroelectric nature of the KNNLN ceramic in its bulk form. The AD film exhibited a large recoverable energy density of 23.4 J/cm3, with an efficiency of over 70% under the electric field of 1400 kV/cm. Besides, an ultrahigh power density of 38.8 MW/cm3 together with a fast discharge speed of 0.45 μs, good fatigue endurance (up to 106 cycles), and thermal stability in a wide temperature range of 20–160 °C was also observed. Using the AD process, we could make a highly dense microstructure of the film containing nano-sized grains, which gave rise to the quasi-relaxor ferroelectric characteristics and the remarkable energy storage properties.