The hot corrosion of Co-25Cr-10Ni-5Ta-3Al-0.5Y alloy /S-57

A cobalt-base alloy, Co-25Cr-10Ni-5Ta-3Al-0.5Y (S-57), was subjected to hot corrosion in Mach 0.3 burner-rig combustion gases at maximum alloy temperatures of 900 and 1000 C. Various salt concentrations were injected into the burner: 0.5, 2,5, and 10 parts per million synthetic sea salt and 4 parts...

Full description

Saved in:
Bibliographic Details
Published in:Corrosion science 1978-01, Vol.18, p.651-677
Main Author: Santoro, G J
Format: Article
Language:English
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:A cobalt-base alloy, Co-25Cr-10Ni-5Ta-3Al-0.5Y (S-57), was subjected to hot corrosion in Mach 0.3 burner-rig combustion gases at maximum alloy temperatures of 900 and 1000 C. Various salt concentrations were injected into the burner: 0.5, 2,5, and 10 parts per million synthetic sea salt and 4 parts per million sodium sulfate (Na2SO4). The extent of corrosion was determined by measuring the maximum depth of corrosion in the alloy, and the corrosion process was studied by metallography, X-ray diffraction, scanning electron microscopy, and electron microprobe analysis. While S-57 was found to possess only moderate oxidation resistance at these temperatures, this alloy resisted significant hot corrosion attack under all but the most severe test conditions. The process of hot corrosion attack under the most severe conditions of this study was primarily sulfidation.
ISSN:0010-938X