High temperature oxidation of a commercial Cr-Mn austenitic steel in air

• Published in: Materials and corrosion 1987-07, Vol.38 (7), p.368-375
• Main Authors: Gesmundo, F., De Asmundis, C., Battilana, G., Ruedl, E.
• Format: Article
• Language: English
• Subjects: Applied sciences; Corrosion; Corrosion mechanisms; Cross-disciplinary physics: materials science; rheology; Exact sciences and technology; Materials science; Metals, semimetals and alloys; Metals. Metallurgy; Physics; Specific materials
• ISSN: 0947-5117; 0043-2822; 1521-4176
• DOI: 10.1002/maco.19870380705

The oxidation of an austenitic steel containing 18% chromium and 12.3% manganese at 800‐1000°C in air occurs at a slower rate than that of a steel containing 9.5% chromium and 17.5% manganese. However, the rate of corrosion of this 18% chromium alloy is still large in comparison with the case of formation of a continuous chromia scale at the base of the scale layer. This result is attributed to the negative effect of the manganese on the thermodynamic stability of Cr2O3. Hochtemperaturoxidation eines handelsüblichen austenitischen CrMn‐Stahls an Luft Die Oxidation eines austenitischen Stahls mit 18% Chrom und 12,3% Mangan bei 800 bis 1000°C in Luft erfolgt mit geringerer Geschwindigkeit als die eines die eines Stahls mit 9,5% Chrom und 17,5% Mangan. Trotzdem ist die Korrosionsgeschwindigkeit dieses 18% Cr‐Stahls noch hoch im Vergleich zu der Korrosion, die bei der Bildung einer kontinuierlichen Chromoxidschicht unterhalb der Zunderschicht auftreten würde. Dieses Ergebnis wird dem negativen Einfluß von Mangan auf die thermodynamische Stabilität von Cr2O3 zugeschrieben.