A Stable NanoPAA-ZnO/ZnCl2 Composite with Variable 3D Structured Morphology and Sustained Superhydrophilicity

• Published in: Langmuir 2021-05, Vol.37 (18), p.5457-5463
• Main Authors: Zhou, Yukun, Dang, Yang, Wang, Kaige, Zhao, Wei, Zhang, Chen, Jiao, Yang, Feng, Xiaoqiang, Wang, Guiren, Shen, Tiehan H
• Format: Article
• Language: English
• ISSN: 0743-7463; 1520-5827
• DOI: 10.1021/acs.langmuir.0c03257

A ZnO/ZnCl2 composite with stable 3D structural morphologies and long lasting superhydrophilicity was synthesized on the top surface of a nano porous anodic alumina (nanoPAA) substrate. The wettability of a nanoPAA-ZnO/ZnCl2 was systematically characterized and the experimental data indicated that the water contact angle (WCA) of 0° could be achieved as well as maintained over 7 days and still remained at 4.36° after 50 days, and its 3D structural morphology had no clearly observable change during this period. The mechanism for the superhydrophilicity of the composites was interpreted in terms of the inherent hydrophilicity of ZnO/ZnCl2 nanofilm, the three-dimensional structures of wrinkled nanoflakes, the nanogaps between neighbor nanoflakes, the difference of structual morphologies (i.e., size, shape, and upright posture of nanoflakes), and the measured True Volume of voids in the nanocomposite. The structural morphologies were mainly determined by the parameters such as the original concentration of precursor ZnCl2 and the pore diameter of nanoPAA substrate. The study proposes a promising superhydrophilic nanomaterial and a cost-effective synthesis method, which will play a practical role in the fields of biomedical molecular sensors and micro/nanofluidic chips.