Structure-property relationships in 3D-printed poly(l-lactide-co-ε-caprolactone) degradable polymer

The recent growth of polymer 3D-printing has brought innovation to the medical implant field. Implants with complex porous structures can be fabricated by printing to tune mechanical behavior and enable diffusion, consequently improving integration with tissues in the human body. Poly(L-lactide-co-ε...

Full description

Saved in:
Bibliographic Details
Published in:Journal of the mechanical behavior of biomedical materials 2021-09, Vol.121, p.104650-104650, Article 104650
Main Authors: Bachtiar, Emilio Omar, Ritter, Virginia Cary, Gall, Ken
Format: Article
Language:English
Subjects:
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:The recent growth of polymer 3D-printing has brought innovation to the medical implant field. Implants with complex porous structures can be fabricated by printing to tune mechanical behavior and enable diffusion, consequently improving integration with tissues in the human body. Poly(L-lactide-co-ε-caprolactone) (PLCL) is a 3D-printable polymer that possess a wide range of possible mechanical properties depending on its monomer composition. It is often used in biomedical applications requiring degradability. In this study, we explore 1) the effect of annealing 3D-printed PLCL and 2) the degradation profile of both annealed and unannealed 3D-printed PLCL scaffolds. The degraded samples were characterized for its molecular weight, mass loss, microstructure, and mechanical properties. By annealing the 3D-printed PLCL, we reveal the structure-property relationship of PLCL. Crystallization was found to be a crucial factor in the resulting mechanical properties, increasing stiffness significantly. The subsequent degradation study revealed that there was no significant difference brought about by pre-annealing the scaffolds. The scaffolds were found to maintain their mechanical properties until up to 8 weeks, at which point the scaffolds reached a critical molecular weight and lost their mechanical integrity.
ISSN:1751-6161
1878-0180
DOI:10.1016/j.jmbbm.2021.104650