Effect of partially stabilized zirconia thickness on the translucency and microhardness of resin cement

• Published in: The Journal of prosthetic dentistry 2024-01, Vol.131 (1), p.94-99
• Main Authors: Olcay, Emin Orkun, Diken Turksayar, Almira Ada, Demirel, Munir, Donmez, Mustafa Borga, Şahmalı, Sevil Meral
• Format: Article
• Language: English
• ISSN: 0022-3913; 1097-6841
• DOI: 10.1016/j.prosdent.2022.01.030

Partially stabilized zirconia has been introduced as a more translucent iteration. However, knowledge of the effect of the thickness of partially stabilized zirconia on the microhardness of resin cement is sparse. The purpose of this in vitro study was to evaluate the effect of thickness and material type on the translucency of partially stabilized zirconia and the microhardness of the resin cement polymerized beneath. Specimens were prepared from 2 translucent zirconias with different yttrium content (Ceramil Zolid HT+ [HT] and Ceramil Zolid FX [SHT]) and a lithium disilicate glass-ceramic (e.max CAD [EX]) of different thicknesses (0.5, 1, 1.5, and 2 mm) (n=10). Color coordinates were recorded by using a spectrophotometer, and the relative translucency parameter (RTP) was calculated by using the CIEDE2000 formula. The microhardness of the resin cement polymerized under ceramic specimens was measured. Two-way analysis of variance, the Tukey honestly significant difference, and independent samples t tests were used to analyze the data (α=.05). Material type (P