Phosphate-Based Cross-Linked Polymers from Iodo–ene Photopolymerization: Tuning Surface Wettability through Thiol–ene Chemistry

• Published in: ACS macro letters 2019-02, Vol.8 (2), p.213-217
• Main Authors: Sinha, Jasmine, Fairbanks, Benjamin D, Song, Han Byul, Bowman, Christopher N
• Format: Article
• Language: English
• ISSN: 2161-1653; 2161-1653
• DOI: 10.1021/acsmacrolett.8b00934

Motivated by the various reported potential applications of poly­(phosphine oxide) materials, a visible light photoinitiated iodo–ene reaction was successfully employed in network polymerization between the phosphorus-containing multifunctional monomer, tris­(allyloxymethyl)­phosphine oxide (TAOPO), and diiodoperfluorobutane. The cross-linked poly­(phosphine oxide) network exhibited a higher glass transition temperature than a similarly cross-linked polymer formulated with trimethylolpropane triallyl ether (TMPTAE). Interestingly, the TMPTAE/DIPFB cross-linked polymer, changed color from clear to yellow within 10 min of exposure to air, whereas the cross-linked poly­(phosphine oxide) underwent a similar change only upon heating. Upon investigation, it was determined that alkenes were generated within the polymer network, presumably via elimination, accounting for the observed color. These double bonds, formed in the polymer matrix, permitted surface modification via radical thiol–ene reaction. The successful surface functionalization with PEG-SH resulted in increasing the surface wettability. Additionally, the phosphorus-containing network polymer with double bonds in the polymer matrix showed shape memory capability, this representing an exciting and versatile materials platform.