The effect and mechanism of bismuth doped lead oxide on the performance of lead-acid batteries

• Published in: Journal of power sources 2001-03, Vol.95 (1), p.108-118
• Main Authors: Chen, H.Y, Wu, L, Ren, C, Luo, Q.Z, Xie, Z.H, Jiang, X, Zhu, S.P, Xia, Y.K, Luo, Y.R
• Format: Article
• Language: English
• Subjects: Applied sciences; Bismuth; Capacity; Cycle-life; Direct energy conversion and energy accumulation; Electrical engineering. Electrical power engineering; Electrical power engineering; Electrochemical conversion: primary and secondary batteries, fuel cells; Exact sciences and technology; Lead oxide; Lead-acid battery; Water loss
• ISSN: 0378-7753; 1873-2755
• DOI: 10.1016/S0378-7753(00)00640-6

Flooded automotive and motorcycle lead-acid batteries were manufactured from three kinds of lead oxides including electrolyzed pure lead (99.99 wt.% Pb) oxide, electrolyzed pure lead oxide doped with Bi 2O 3 (0.02 wt.% Bi 2O 3) and bismuth-bearing refined lead (0.02 wt.% Bi) oxide. The first cranking and cold cranking curves of the automotive batteries show that there is no obvious difference among the above lead oxides. Bismuth in lead oxide does not affect the water loss of flooded batteries. However, bismuth results in the improvement of capacity and charge-acceptance capability. In discharge, the positive voltage versus cadmium of plates with bismuth decreases more slowly than that of plates without bismuth. In order to investigate the mechanism of the function of bismuth, three other kinds of test electrodes were prepared from electrolyzed pure lead (99.99 wt.% Pb) oxide, electrolyzed pure lead oxide doped 0.02 wt.% Bi 2O 3 and electrolyzed pure lead oxide doped 0.06 wt.% Bi 2O 3. The cyclic voltammetry curve shows that bismuth has no significant influence on the electrochemical behavior of the positive active-material. There is an opposite result concerning the cathodic polarization curves between bismuth doped in the electrode and Bi 3+ ion doped in the electrolyte. Bismuth doped in the electrode results in a decrease of the hydrogen overpotential. Conversely, Bi 3+ ion doped in the electrolyte results is an increase. The chemical analysis confirms that a trace of Bi 3+ ion exists in sulfuric acid solution (e.g. plates soaking, after formation, after cycling). A higher porosity is observed in the positive active-material containing bismuth by SEM technique. SEM morphology shows that needle-like crystals begin to occur after a few cycles. X-ray diffraction phase analysis proves that the amount of α-PbO 2 is increased by doping bismuth in to lead oxide. The existing forms, chemical characteristics and electrochemical reactions of bismuth during manufacture and are of lead-acid batteries are demonstrated clearly. The mechanism of the function of bismuth improving capacity, prolonging cycle-life and reducing water loss has been elucidated in detail.