Alkali treatment of jute fibers: Relationship between structure and mechanical properties

• Published in: Journal of applied polymer science 1999-01, Vol.71 (4), p.623-629
• Main Authors: Gassan, Jochen, Bledzki, Andrzej K.
• Format: Article
• Language: English
• Subjects: alkali treatment; Applied sciences; Compounding ingredients; Exact sciences and technology; Fillers and reinforcing agents; natural fibers; Polymer industry, paints, wood; structure-property relationships; Technology of polymers
• ISSN: 0021-8995; 1097-4628
• DOI: 10.1002/(SICI)1097-4628(19990124)71:4<623::AID-APP14>3.0.CO;2-K

The mechanical properties of tossa jute fibers were improved by using NaOH treatment process to improve the mechanical properties of composites materials. Shrinkage of fibers during this process has significant effects to the fiber structure, as well as to the mechanical fiber properties, such as tensile strength and modulus. Isometric NaOH‐treated jute yarns (20 min at 20°C in 25% NaOH solution) lead to an increase in yarn tensile strength and modulus of ∼ 120% and 150%, respectively. These changes in mechanical properties are affected by modifying the fiber structure, basically via the crystallinity ratio, degree of polymerization, and orientation (Hermans factor). Structure–property relationships, developed for cellulosic man‐made fibers, were used with a high correlation factor to describe the behavior of the jute fiber yarns. © 1999 John Wiley & Sons, Inc. J Appl Polym Sci 71: 623–629, 1999