The wear of ultrafine WC–Co hard metals

• Published in: Wear 2001-10, Vol.250 (1-12), p.604-610
• Main Authors: Allen, C., Sheen, M., Williams, J., Pugsley, V.A.
• Format: Article
• Language: English
• Subjects: Abrasion; Erosion; Tungsten carbide; Ultrafine grains
• ISSN: 0043-1648; 1873-2577
• DOI: 10.1016/S0043-1648(01)00667-6

The wear performance of ultrafine-grained tungsten carbide–cobalt (WC–Co) hard metals during three-body abrasion and particle erosion has been evaluated and compared to that of similar conventional coarser grained hard metals. The tungsten carbide grain size varied between 0.5 and 3μm with cobalt contents ranging from 6 to 15%. Silica particles were used in both forms of testing. Erosion was carried out at 60ms−1 at an impact angle of 75° and abrasion at a velocity of 0.5ms−1 and a load of 50N. The wear resistance of the ultrafine grades was found to be at least double that of the closest conventional fine grained hard metals. These increases in wear performance are considerably higher than any corresponding increase in hardness which is, at most, 25% and is not achieved at the expense of fracture toughness which is maintained at a similar level to that of conventional fine grained hard metals. The increase in wear resistance coincides with a change in the mechanism of material removal. Sub-micron materials experience ductile deformation and bulk removal of material whilst coarser grades display more localised response with extensive fragmentation of the WC grains.