Processing, sintering characteristics and dielectric properties of barium-substituted Pb(Mg1/3Nb2/3)O3-PbTiO3 solid solution

• Published in: Journal of materials science 1997, Vol.32 (14), p.3753-3758
• Main Authors: GUHA, J. P, HAERTLING, G. H
• Format: Article
• Language: English
• Subjects: Applied sciences; Barium oxides; Building materials. Ceramics. Glasses; Ceramic industries; Chemical industry and chemicals; Composition; Curie temperature; Dielectric properties; Electrotechnical and electronic ceramics; Exact sciences and technology; Lead; Lead titanates; Materials science; Perovskites; Relaxors; Roasting; Sintering; Solid solutions; Substitutes; Technical ceramics; Theoretical density
• ISSN: 0022-2461; 1573-4803
• DOI: 10.1023/A:1018615421299

Solid solutions in the lead-based relaxor system Pb(Mg1/3Nb2/3)O3–PbTiO3 were modified by minor substitutions of Ba in the Pb-site of the perovskite lattice. The modified compositions were calcined at 830 °C for 3 h to yield fine-grained, single-phase perovskite materials. A small amount of excess MgO(0.05 wt %), which mostly served as a sintering aid, was added to the calcined batches and the resulting mixtures were sintered at temperatures between 1150 and 1250 °C for periods ranging from 3 to 5 h. The substitutions of BaO for PbO in the perovskite solid solution lattice caused a progressive lowering of the Curie point with increasing BaO content. On average, the Curie point decreased by about 10 °C for each mole of BaO substituted for PbO. Among the various Ba-substituted solid solutions studied, the one with a nominal composition Pb0.99Ba0.01[(Mg1/3Nb2/3)0.9Ti0.1]O3 which has a Curie point located near 28 °C, exhibited excellent dielectric properties. On sintering at 1250 °C for 3 h, this composition yielded a density near 96% of the theoretical density. The peak dielectric constant of the composition at 1 KHz was slightly higher than 22000, and the corresponding tan δ value was 1.5% with a specific resistivity of 2.5 × 1012 Ω cm-1.