Influence of polymerization conditions on the hydrolytic degradation of poly( dl-lactide) polymerized in the presence of stannous octoate or zinc-metal

Laboratory- and pilot-scale racemic polylactides (PLA50) were synthesized in the presence of stannous octoate (SnOct 2) or zinc-metal as initiators in the absence of alcohol. The resulting polymers were processed by compression molding or injection molding depending on the batch scale. The hydrolyti...

Full description

Saved in:
Bibliographic Details
Published in:Biomaterials 2002-02, Vol.23 (4), p.993-1002
Main Authors: Schwach, Grégoire, Coudane, Jean, Engel, Robert, Vert, Michel
Format: Article
Language:English
Subjects:
Absorption
Biocompatible Materials - chemistry
Biodegradation, Environmental
Caproates
Crystallization
Degradation
Drug Stability
Hydrolysis
In Vitro Techniques
Lactide
Materials Testing
Molecular Weight
Pilot Projects
Polyesters - chemistry
Polylactide
Stannous octoate
Tin
Water
Zinc
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Laboratory- and pilot-scale racemic polylactides (PLA50) were synthesized in the presence of stannous octoate (SnOct 2) or zinc-metal as initiators in the absence of alcohol. The resulting polymers were processed by compression molding or injection molding depending on the batch scale. The hydrolytic degradation of compression-molded samples selected to be comparable was investigated first in order to show the influence of the initiator system. Differences in water uptake were found between PLA50–Zn (zinc-metal initiation) and PLA50–Sn (SnOct 2 initiation), PLA50–Zn being much more hydrophilic. PLA50–Sn exhibited a slower molecular weight decrease and delayed onsets of weight loss, release of acidity and stereocomplex formation, with respect to PLA–Zn. The concentration in residual tin in PLA50–Sn increased from 306 to 795 ppm during aging. In the case of PLA50–Zn the residual metal remains constant at ca. 40 ppm. In a second series of experiments, high molecular weight PLA50 different in characteristics and in initiator, synthesized under pilot-scale, were compared. The effects of the initiator on the degradation of the polymers well agreed with laboratory-scale findings, differences in hydrophobicity being enlarged by the up scaling. PLA50–Sn polymers appeared much more degradation resistant than PLA50–Zn ones. Contributions of the other characteristics (e.g. molecular weight, purity, stereoregularity, processing) were shown to be important as well.
ISSN:0142-9612
1878-5905
DOI:10.1016/S0142-9612(01)00209-5