Phase and Microstructural Development of Sol-gel-derived Strontium Barium Niobate Thin Films

Microstructural changes in sol-gel-derived SrxBa1−xNb2O6 (SBN) thin films were monitored as a function of Ba-to-Sr ratio (from x = 0 to x = 1), choice of substrate (Si or MgO), and processing variations. Sols were created using Ba, Sr, and Nb alkoxides dissolved in acetic acid. The relatively high d...

Full description

Saved in:
Bibliographic Details
Published in:Journal of materials research 2000-06, Vol.15 (6), p.1417-1423
Main Authors: Oral, A. Y., Mecartney, M. L.
Format: Article
Language:English
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Microstructural changes in sol-gel-derived SrxBa1−xNb2O6 (SBN) thin films were monitored as a function of Ba-to-Sr ratio (from x = 0 to x = 1), choice of substrate (Si or MgO), and processing variations. Sols were created using Ba, Sr, and Nb alkoxides dissolved in acetic acid. The relatively high decomposition temperature for the organics led to a tendency to form defects, but careful control of thermal process parameters could be used to produce a uniform film microstructure. An unexpected phase, interpreted as a hexagonal (pseudo-orthorhombic) variant of hexagonal BaNb2O6, was encountered in Ba-rich sol-gel-derived SBN powders and thin films annealed at 750 °C. Increased (001) orientation was observed for SBN thin films deposited on (100) MgO when fast thermal processing was used.
ISSN:0884-2914
2044-5326
DOI:10.1557/JMR.2000.0205