Transverse tension fatigue life characterization through flexure testing of composite materials

• Published in: International journal of fatigue 2002-02, Vol.24 (2), p.127-145
• Main Authors: O'Brien, T.Kevin, Chawan, Arun D, Krueger, Ronald, Paris, Isabelle L
• Format: Article
• Language: English
• Subjects: Applied sciences; Carbon–epoxy; Composite materials; Exact sciences and technology; Fatigue life; Forms of application and semi-finished materials; Glass–epoxy; Laminates; Polymer industry, paints, wood; Technology of polymers; Transverse tension strength; Weibull scaling law
• ISSN: 0142-1123; 1879-3452
• DOI: 10.1016/S0142-1123(01)00104-9

The transverse tension fatigue life of S2/8552 glass–epoxy and IM7/8552 carbon–epoxy was characterized using flexure tests of 90-degree laminates loaded in 3-point and 4-point bending. The influence of specimen polishing and specimen configuration on transverse tension fatigue life was examined using the glass–epoxy laminates. Results showed that 90-degree flexure specimens with polished machined edges and polished tension-side surfaces had lower fatigue lives than unpolished specimens when cyclically loaded at equal stress levels. The influence of specimen thickness and the utility of a Weibull scaling law were examined using the carbon–epoxy laminates. The influence of test frequency on fatigue results was also documented for the 4-point bending configuration. A Weibull scaling law was used to predict the 4-point bending fatigue lives from the 3-point bending curve fit and vice versa. Scaling was performed based on maximum cyclic stress level as well as fatigue life. The scaling laws based on stress level shifted the curve fit S–N characterizations in the desired direction, however, the magnitude of the shift was not adequate to accurately predict the fatigue lives. Furthermore, the scaling law based on fatigue life shifted the curve fit S–N characterizations in the opposite direction from measured values. Therefore, these scaling laws were not adequate for obtaining accurate predictions of the transverse tension fatigue lives of heterogeneous, fiber reinforced, polymer matrix composites.