Tensile and wear properties of aluminum composites
Beryl/Al–Si–Mg composites containing 2.0–10.0% of beryl particles have been fabricated by squeeze casting. Pressure of 80 MPa was maintained during solidification in a specially designed die and punch maintained at 400 °C. The tensile and wear properties have been evaluated and compared with gravity...
Saved in:
Published in: | Wear 2003-08, Vol.255 (1), p.638-642 |
---|---|
Main Authors: | , , , |
Format: | Article |
Language: | English |
Subjects: | |
Citations: | Items that this one cites Items that cite this one |
Online Access: | Get full text |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | Beryl/Al–Si–Mg composites containing 2.0–10.0% of beryl particles have been fabricated by squeeze casting. Pressure of 80
MPa was maintained during solidification in a specially designed die and punch maintained at 400
°C. The tensile and wear properties have been evaluated and compared with gravity cast beryl–aluminum composites. The squeeze cast composites show a peak strength of 216
MPa showing an increase of 11.6% in tensile strength. The new composites also have improved wear resistance when compared to gravity cast composites. Squeeze cast composites with 6
wt.% of beryl particles showed almost 1.2 times reduced adhesive wear rate at 2400
m sliding distance when compared to that at 600
m. |
---|---|