Corrosion protection of magnetron sputtered TiN coatings deposited on high strength aluminium alloys

TiN x coatings were deposited on aluminium AA7075-T6 substrates by reactive DC magnetron sputtering. The main objective was to improve the impermeability to corrosive media by controlling the morphology of the coatings. It was found that by increasing the bias voltage during deposition to −150 V the...

Full description

Saved in:
Bibliographic Details
Published in:Surface & coatings technology 2004-01, Vol.177, p.399-403
Main Authors: Diesselberg, M., Stock, H-R., Mayr, P.
Format: Article
Language:English
Subjects:
Aluminium alloys
Corrosion
Magnetron sputtering
TiN coatings
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:TiN x coatings were deposited on aluminium AA7075-T6 substrates by reactive DC magnetron sputtering. The main objective was to improve the impermeability to corrosive media by controlling the morphology of the coatings. It was found that by increasing the bias voltage during deposition to −150 V the normally arising columnar structure is reduced due to enhanced defect and nucleation site formation. In consequence these coatings exhibit a reduced porosity and therefore fewer possible paths for corrosive media like aqueous sodium chloride solution to reach the interface substrate/coating. A further effective improvement of the corrosion behaviour compared to stoichiometric TiN coatings was achieved by decreasing the nitrogen content in the TiN x layers below 20 at.% N. This has been confirmed by potentiodynamic measurements as well as salt spray tests. It is proposed that this further improvement is due to the formation of a thicker and denser surface oxide layer as soon as the coating is exposed to air.
ISSN:0257-8972
1879-3347
DOI:10.1016/j.surfcoat.2003.09.015