Mn4+-Activated Double-Perovskite-Type Sr2LuNbO6 Multifunctional Phosphor for Optical Probing and Lighting

• Published in: ACS applied materials & interfaces 2023-06, Vol.15 (23), p.28193-28203
• Main Authors: Chen, Zhanglin, Du, Songmo, Zhu, Kaiming, Tian, Zhaobo, Zhang, Jie, Li, Fei, Zhang, Shijia, Zhao, Shuo, Cui, Wei, Yuan, Xuanyi, Chen, Kexin, Yuan, Guoliang, Liu, Guanghua
• Format: Article
• Language: English
• Subjects: Functional Inorganic Materials and Devices
• ISSN: 1944-8244; 1944-8252
• DOI: 10.1021/acsami.3c03897

Multifunctional phosphors have significant application and scientific value and are becoming a research hotspot in the field of luminescent materials. Herein, we report Mn4+-activated double-perovskite-type Sr2LuNbO6 multifunctional phosphors with excellent comprehensive properties in the fields of optical temperature/pressure sensing and w-LED lighting. The crystalline structure, elemental composition, optimal doping concentration, crystal-field strength, and optical bandgap of the phosphors are investigated in detail, and the mechanisms of concentration and thermal quenching are discussed. From the optimal Sr2LuNb0.998O6:0.2%Mn4+ phosphor, a LED lamp for indoor warm-white lighting is successfully fabricated. Further, the thermometric properties of the phosphors are explored for applications as FIR- and lifetime-based thermometers, showing a maximum relative sensitivity of 1.55% K–1 at 519 K. Upon pressure loading, a significant red-shift of the peak centroid is observed, and the pressure sensitivity is determined to be 0.82 nm/GPa. These results suggest that the Mn4+-activated Sr2LuNbO6 multifunctional phosphors have great potential to be utilized in the fields of optical thermometry, manometry, and lighting.