The tensile properties of AISI 316L and OPTIFER in various conditions irradiated in a spallation environment

• Published in: Journal of nuclear materials 2005-08, Vol.343 (1), p.236-240
• Main Authors: Chen, J., Rödig, M., Carsughi, F., Dai, Y., Bauer, G.S., Ullmaier, H.
• Format: Article
• Language: English
• Subjects: Applied sciences; Controled nuclear fusion plants; Energy; Energy. Thermal use of fuels; Exact sciences and technology; Fission nuclear power plants; Fuels; Installations for energy generation and conversion: thermal and electrical energy; Nuclear fuels
• ISSN: 0022-3115; 1873-4820
• DOI: 10.1016/j.jnucmat.2004.10.168

Tensile specimens, prepared from AISI 316L austenitic stainless steel in three conditions (solution-annealed, cold-worked and electron-beam welded) and from OPTIFER martensitic stainless steel in tempered condition, were irradiated in the Swiss spallation neutron source (SINQ) at 90–400 °C to displacement doses from 3 dpa to 11 dpa. The mechanical properties were measured by tensile testing at room temperature and 250 °C, respectively, and subsequent metallographic analysis was employed. The tensile results indicated that the strength of AISI 316L-SA is quite similar or a little higher than in 316L-EBW but elongation of SA 316L is somewhat larger than EBW for both unirradiated and irradiated samples. The cold-worked specimens revealed much higher strength but almost zero strain-to-necking after irradiation. The results from OPTIFER samples showed that irradiation hardening increases with dose, which is accompanied by a dramatic reduction of uniform elongation beginning at very low dose. The metallographic analysis showed that the samples of AISI 316L-EBW failed in the welded zone.