Evaluation of enamel wear by 3 occlusal splint materials: An in vitro study

• Published in: The Journal of prosthetic dentistry 2023-11, Vol.130 (5), p.743-743.e6
• Main Authors: Borg, Hisham, Azer, Shereen S., El Hadary, Amany, Helaly, Osama, Shoeib, Ahmad, Hassan, Mohammed
• Format: Article
• Language: English
• ISSN: 0022-3913; 1097-6841
• DOI: 10.1016/j.prosdent.2023.08.034

Occlusal devices used to manage bruxism have been commonly fabricated from polymethyl methacrylate with the powder-liquid technique. More recently, Vertex ThermoSens (VTS) and the biocompatible high-performance polymer (BioHPP), an optimized material having polyetheretherketone (PEEK) as its basis, have been used, but little is known about the wear of these materials on human enamel. The purpose of this in vitro study was to assess via a mastication simulation test how 3 occlusal device materials affected the wear and roughness of enamel antagonists. A noncontact 3D optical profilometer was used to measure the enamel surface roughness (Ra) against 3 occlusal device materials: vertex regular, VTS, and PEEK high-performance polymer (BioHPP). A dual-axis mastication simulator was used to perform a 2-body wear test on specimens from each group. The test consisted of 10 000 cycles with a 70-N force and 5 to 55 °C thermocycling. Following simulated mastication, the weight of each specimen and the Ra change were compared with the Kolmogorov-Smirnov test, paired specimens t test, Wilcoxon signed-rank test, and 1-way analysis of variance (α=.05). The polyamide group caused the lowest amount of enamel wear (P