High-Speed and Ultrasensitive Solar-Blind Ultraviolet Photodetectors Based on In Situ Grown β‑Ga2O3 Single-Crystal Films

• Published in: ACS applied materials & interfaces 2024-02, Vol.16 (5), p.6068-6077
• Main Authors: Chen, Tiwei, Zhang, Xiaodong, Zhang, Li, Zeng, Chunhong, Li, Shaojuan, Yang, An, Hu, Yu, Li, Botong, Jiang, Ming, Huang, Zijing, Li, Yifei, Guo, Gaofu, Fan, Yaming, Shi, Wenhua, Cai, Yong, Zeng, Zhongming, Zhang, Baoshun
• Format: Article
• Language: English
• Subjects: Functional Inorganic Materials and Devices
• ISSN: 1944-8244; 1944-8252
• DOI: 10.1021/acsami.3c15561

Deep-level defects in β-Ga2O3 that worsen the response speed and dark current (I d) of photodetectors (PDs) have been a long-standing issue for its application. Herein, an in situ grown single-crystal Ga2O3 nanoparticle seed layer (NPSL) was used to shorten the response time and reduce the I d of metal–semiconductor-metal (MSM) PDs. With the NPSL, the I d was reduced by 4 magnitudes from 0.389 μA to 81.03 pA, and the decay time (τd1/τd2) decreased from 258/1690 to 62/142 μs at −5 V. In addition, the PDs with the NPSL also exhibit a high responsivity (43.5 A W−1), high specific detectivity (2.81 × 1014 Jones), and large linear dynamic range (61 dB) under 254 nm illumination. The mechanism behind the performance improvement can be attributed to the suppression of the deep-level defects (i.e., self-trapped holes) and increase of the Schottky barrier. The barrier height extracted is increased by 0.18 eV compared with the case without the NPSL. Our work contributes to understanding the relationship between defects and the performance of PDs based on heteroepitaxial β-Ga2O3 thin films and provides an important reference for the development of high-speed and ultrasensitive deep ultraviolet PDs.